Resistance to Corrosion and Oxidation of Inconel 718
Inconel 718 has good resistance to oxidation and corrosion at temperatures in the alloy’s useful strength range in atmospheres encountered in jet engines and gas turbine operations.
Physical Properties of Inconel 718
Typical physical properties of Inconel 718 are summarized in the table below.
| Solution Treated | Solution Treated and Aged | |
| Density | 0.296 lb/in3 (8.192 g/cm3) | 0.297 lb/in3 (8.22 g/cm3) |
| Specific Gravity | 8.19 | 8.22 |
| Melting Range | 2500-2600°F | 1370-1430°C |
Thermal Conductivity of Inconel 718
The thermal conductivity at various temperatures for Inconel 718 are given in the following table.
| Temperature Range | Co-Efficients | ||
| °C | °F | W/m.K | Btu.ft/ft2.hr.°F |
| 0-100 | 532-212 | 6.5 | 11.2 |
Mechanical Properties
The room temperature strength of the Inconel 718 alloy is substantially increased by precipitation heat treatment as the following data indicate. These values are properties specified for sheet, strip and plate in AMS 5596 and AMS 5597.
| Yield Strength Min (0.2% offset) |
Ultimate Tensile Strength Min |
Elongation (% in 2″) |
|
| Sheet and strip | 80,000 psi (550 MPa) | 140,000 psi (965 MPa) | 30 (min) |
| Plate | 105,000 psi (725 MPa) | 150,000 psi (1,035 MPa) | 30 (min) |
Solution trated plus precipitation heat treated.
| Yield Strength Min (0.2% offset) |
Ultimate Tensile Strength Min |
Elongation (% in 2″) |
| 150,000 (1,035 MPa) | 180,000 psi (1,240 MPa) | 12 (min) |
Typical short time tensile properties of Inconel 718 as a function of temperature are shown here for material solution treated and aged as follows:
- Solution Treatment: 1800°F (982°C) 1 hour
- Precipitation Treatment: 1325°F (718°C) 8 hours, Furnace Cool at 100°F (55°C) per hour to 1150°F (621°C) 8 hours
Standards
United Performance Metals Inconel 718 is supplied to AMS 5596/5597 and has a UNS designation N07718.
Applications of Inconel 718
Inconel 718 is typically used for:
- Jet engine
- Gas turbine operations